Електроди зварювальні АНО-36

AWS А5.1: Е6013
EN ISO 2560-A-E 42 0 RC 1 1
CONDITIONS OF USE
  • intended for welding corner, butt and butt joints of metal up to 20 mm thick;
  • with assembly welding, work is possible in all spatial positions without a significant change in the welding current
  • electrodes with a diameter of 3.0 mm to 4.0 mm are suitable for welding in all spatial positions except vertical, by the top-down method
  • electrodes with a diameter of 5.0 mm - for the lower, horizontal on a vertical plane and vertical by the bottom-up position.
  • welding of vertical seams by the top-down method is performed with a short arc or abutment, at the same time, the electrode should be located in a plane that divides the angle of the welding parts in half, and the angle of elevation of the electrode to the vertical should be 40...70°
  • to increase penetration, do not allow slag to flow in front of the arc
SPECIAL PROPERTIES
  • are distinguished by easy initial and re-ignition, soft and stable arc burning, ensure small losses of metal from spattering, uniform melting of the coating, excellent formation of the weld metal, easy separation of the slag crust
  • welding can be performed from power sources that are included in both industrial and household networks
  • reduce the requirements for personnel qualification
  • electrodes are not sensitive to the quality of edge preparation, the presence of rust and other contamination of the surface of the welding metal
  • surfacing coefficient: 0.13...0.15 g/A•min
  • consumption of electrodes per 1 kg of deposited metal: 1.4...1.7 kg
АНО-36 electrodes are designed for manual arc welding on direct or alternating current of ordinary and responsible structures from low-carbon grades of steel, supplied according to DSTU 2651 / GOST 380 (St 0, St 1, St 2, St 3 of all groups A, B, C and all degrees of deoxidation - "KP", "PS", "SP") and according to DSTU 7809 (05kp, 08kp, 08ps, 08, 10kp, 10ps, 10, 15kp, 15ps, 15, 20kp, 20ps, 20).
Package Weight
First select diameter
Packaging data
Diameter, mm Length, mm Number of electrodes in a pack, pcs. Pack weight, kg
3.0 350 36…38;92…96 1.0; 2.5
4.0 450 84…86 5.0
Package Weight
First select diameter
Type of coating
rutile-cellulosic
Weld metal chemical composition, %
According to AWS A5.1 / Typical results
C
Carbon
≤ 0,11
Mn
Manganese
0,40…0,65
Si
Silicon
0,10…0,35
P
Phosphorus
≤ 0,035
S
Sulfur
≤ 0,030
Weld metal mechanical properties
According to AWS A5.1 / Typical results
  • Tensile strength, MPa: 500…640
  • Yield strength, MPa: ≥ 420
  • Elongation, %: ≥ 22
  • Impact strength KCU +20 ˚С, J / cm²: ≥ 78
  • Impact energy KV 0 ˚С, J ≥ 47
Re-drying before welding
  • permissible moisture content in the coating before use is no more than 0,9 %
  • if the electrode coating is moistened above normal, dry for 60 minutes at 120±10 °С
Welding parameters
Welding current strength, A for electrodes with a diameter of, mm
3.0 mm 4.0 mm 5.0 mm
70 – 110 100 – 150 140 – 210
Welding should be carried out with direct current of any polarity (reverse is recommended, "+" on the electrode) or with alternating current with a no-load voltage of the current source of 50 V.
WELDING POSITIONS
PA
PB
PC
PF
PG
PE
PD