Електроди зварювальні Monolith ЦЛ-11 Плазма

AWS A5.4: E 347-16
EN ISO 3581-А-E 19 9 Nb R 1 2
CONDITIONS OF USE
  • welding is carried out in all spatial positions with direct current of reverse polarity or alternating current from a transformer with an open-circuit voltage of 50±5 V
  • welding must be performed with a short arc without lateral oscillations
SPECIAL PROPERTIES
  • excellent mechanical properties of the deposited metal and increased corrosion resistance in aggressive environments at temperatures up to 450 °С
  • high welding and technological properties, small spattering, easy separation of slag crust and formation of a seam with a smooth transition to the base metal are noted
  • surfacing coefficient: 0,15…0,19 g/A•min
  • consumption of electrodes per 1 kg of deposited metal: 1,3…1,6 кг
Electrodes CL-11 Plasma are designed for welding austenite of corrosion-resistant steels 08Х18Н12Т, 08Х18Н12Б, 03Х18Н11, 06Х18Н11, 08Х18Н12B, 08Х18Н10, 12Х18Н10Т, AISI304, AISI347, etc., operating in aggressive environments at temperatures up to 450°C. They are used for welding containers operating under pressure gas, pipelines, food and petrochemical equipment parts industry, power engineering, energy.
Package Weight
First select diameter
Packaging data
Diameter, mm Length, mm Number of electrodes in a pack, pcs. Pack weight, kg
2.0 300 85…86 1.0
2.5 350 43…46 1.0
3.0 350 30…32 1.0
3.2 350 28…31 1.0
4.0 350 18…19 1.0
Package Weight
First select diameter
Type of coating
rutile
Weld metal chemical composition, %
According to AWS A5.1 / Typical results
C
Carbon
≤ 0,08
Mn
Manganese
≤ 2,0
Si
Silicon
≤ 1,0
P
Phosphorus
≤ 0,030
S
Sulfur
≤ 0,025
Mo
Molybdenum
≤0,75
Cr
Chrome
18,0…21,0
Cu
Copper
≤ 0,75
Ni
Nickel
9,0…11,0
Nb+Ta
Niobium + Tantalum
8ХC до 1,0
Weld metal mechanical properties
According to AWS A5.1 / Typical results
  • Tensile strength, MPa: ≥ 550
  • Yield strength, MPa: ≥ 350
  • Elongation, %: ≥ 25
  • Impact strength KV +20 °C, J ≥ 47
Re-drying before welding
  • permissible moisture content in the coating before use is no more than 0.2%
  • in case of wetting of the electrode coating above the norm - dry for 60 minutes at 400±10 °С
FERRITE NUMBER IN THE DEPOSITED METAL
4-14 FN
Welding parameters
Welding current strength, A for electrodes with a diameter of, mm
2.0 mm 2.5 mm 3.0 mm 3.2 mm 5.0 mm
40-60 50-80 70-100 80-110 90-130
Welding should be carried out with a direct current of reverse polarity, "+" on the electrode, with an arc voltage of 23...27 V or alternating current from a transformer with a no-load voltage of 50 V.
WELDING POSITIONS