Welding electrodes IND RC

AWS A5.1:Е6013

EN ISO 2560-A-E 42 0 RC 1 1

designed for welding fillet, butt and overlapping metal joints up to 20 mm thick
during structural welding, it is possible to work in all spatial positions without significantly changing the welding current
electrodes of 2 to 4 mm diameter are suitable for welding in all spatial positions, and electrodes with a diameter of 5 mm - in all spatial positions except the vertical down one
welding of vertical seams by the vertical down method is carried out with a short arc or with supported electrode, when it is held in a plane that divides the angle of the parts to be welded in half and the vertical lifting angle of the electrode must be equal to 40...70°
to increase the weld penetration, do not allow the slag to flow in front of the arc
welding in a flat position is recommended to be performed in a backhand with angle of 20 – 40° from the vertical to increase the penetration depth and prevent slag from flowing into the bath.

Special properties

they are characterized by easy striking and re-striking , soft and stable arc burning, provide low spatter loss, uniform melting of the coating, excellent weld metal formation, easy separation of the slag
welding can be performed from power sources connected to either commercial or domestic power supply
require less staff qualification skills
the electrodes are not very sensitive to the quality of edge preparation, presence of rust and other contaminants on the surface of the metal to be welded
deposition rate factor: 0,13 – 0,15 g/А·min
consumption of electrodes per 1 kg of deposited metal: 1,4 – 1,7 kg

IND RC electrodes are designed for manual arc welding by reversed or direct current of ordinary and critical structures made of low-carbon steel grades such as DC01, DC04,DD13, FeP01, FeP03, 2c15, C15E2C, C15E, C10, XC10, C20E2C, etc.