Електроди зварювальні Monolith Т-590 Плазма

EN 14700: E Z Fe6
CONDITIONS OF USE
  • the electrode is recommended to be held vertically to the part
  • surfacing should be performed with a very short arc and the lowest possible current to prevent mixing with the base metal
  • to achieve maximum hardness on low-carbon steels it is necessary to carry out surfacing in at least 3 layers.
SPECIAL PROPERTIES
  • the deposited metal can be fired at a temperature of 840...860°С, followed by quenching to a temperature of 950...1000°С, and cooling in lubricant or in air
  • mechanical processing of the deposited metal - only with an abrasive
  • resistance to abrasive wear is very good, resistance to shock loads and corrosion resistance is satisfactory, heat resistance is good
  • surfacing coefficient: 0.13 ... 0.17 g/A•min
  • consumption of electrodes per 1 kg of deposited metal: 1.4...1.6 kg
Electrodes T-590 Plasma are designed for surfacing strengthening materials layers operating under conditions of intense abrasive wear in combination with moderate shock loads. Electrodes are used for surfacing agricultural tools, that works in conditions of moderate humidity, woodworking tools, loading machines, mixers, etc.
Package Weight
First select diameter
Packaging data
Diameter, mm Length, mm Number of electrodes in a pack, pcs. Pack weight, kg
3.0 350 30…32 1.0
4.0 450 14 1.0
Package Weight
First select diameter
Type of coating
rutile-basic
Weld metal chemical composition, %
According to AWS A5.1 / Typical results
C
Carbon
≤2,5
Mn
Manganese
≤3,0
Mo
Molybdenum
≤3,0
P
Phosphorus
≤0,040
S
Sulfur
≤0,040
Cr
Chrome
≤10,0
Nb
Niobium
≤10,0
Re-drying before welding
  • permissible moisture content in the coating before use is no more than 0.4%
  • in case of wetting of the electrode coating above the norm - dry for 60 minutes at 250±20 °С
DEPOSITED WELD METAL HARDNESS
Hardness, HRC without heat treatment after surfacing
48…55
Welding parameters
Welding current strength, A for electrodes with a diameter of, mm
3.0 mm 4.0 mm
90…120 120…150
Welding should be carried out with a direct current of reverse polarity, "+" on the electrode, with a voltage arc of 20...25 V
WELDING POSITIONS
PA
PB
PC
PF
PE
PD