Електроди зварювальні Моноліт ЦЧ-4 Плазма

ISO 1071: E C NiFe – CI 3
AWS A5.15: E NiFe – CI
CONDITIONS OF USE
  • the welding area must be cleaned
  • welding should be performed "cold" or with slight heating
  • direct the rollers only in the longitudinal direction without transverse vibrations of the electrode, in sections of no more than 50 mm
  • in the case of multi-layer surfacing, cool it layer by layer in air to a temperature of 60°C
  • to improve the mechanical properties, immediately heat the roller after welding
SPECIAL PROPERTIES
  • the electrode gives a stable arc and minimal spatter
  • the deposited metal has high strength, resistance to hot cracks, this electrode is suitable for repair welding of parts made of gray, wrought and high-strength cast iron, products that work under high loads
  • surfacing coefficient: 0,13…0,18 g/A•min
  • consumption of electrodes per 1 kg of deposited metal: 1,3…1,6 кг
Electrode with a nickel-iron core, intended for cold welding and surfacing of parts made of gray, forged and high-strength cast iron, as well as welding cast iron with steel.
Package Weight
First select diameter
Packaging data
Diameter, mm Length, mm Number of electrodes in a pack, pcs. Pack weight, kg
2.5 300 58…59 1.0
3.0 350 35…36 1.0
3.2 350 31…32 1.0
4.0 350 20…21 1.0
Package Weight
First select diameter
Type of coating
graphite-basic
Weld metal chemical composition, %
According to AWS A5.1 / Typical results
C
Carbon
0,8…1,5
Mn
Manganese
1,0…2,5
Si
Silicon
≤ 1,0
P
Phosphorus
≤ 0,030
S
Sulfur
≤ 0,030
Ni
Nickel
≥ 52,0
Fe
Ferum
≤ 45,0
Weld metal mechanical properties
According to AWS A5.1 / Typical results
  • Tensile strength, MPa: ≥ 450
  • Yield strength, MPa: ≥ 250
  • Elongation, %: ≥ 10
Re-drying before welding
  • permissible moisture content in the coating before use is no more than 0.5%
  • in case of wetting of the electrode coating above the norm - dry for 60 minutes at 250±10 °С
Welding parameters
Welding current strength, A for electrodes with a diameter of, mm
2.5 mm 3.0 mm 3.2 mm 4.0 mm
50…80 70…100 80…110 120…150
Welding should be carried out with direct current of reverse polarity, "+" on the electrode. or alternating current from a 50 V open-circuit transformer.